PA66 A 216 S30法国罗地亚TECHNYL®表面光洁度好的低翘曲尼龙66塑料（18024445500）

TECHNYL® A 216 S30 　 　 　 　
The values of properties are for natural grade. 　 　 　 　
Properties Standards Unit Values 　
　 　 　 d.a.m*. Cond.**
Physical 　 　 　 　
Water absorption (24 h at 23°C) ISO 62 % 0.75　-
Density ISO 1183-A g/cm3 1.37　-
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 1.60　-
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 1.60　-
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 　 1　-
Mechanical 　 　 　 　
Tensile modulus ISO 527 type 1 A MPa 4500　2500　
Tensile strength at yield ISO 527 type 1 A MPa 80　-
Elongation at yield ISO 527 type 1 A % 4　-
Elongation at break ISO 527 type 1 A % 9　12　
Tensile strength at break ISO 527 type 1 A MPa 80　60　
Flexural modulus ISO 178 MPa 3850　1900　
Flexural maximum stress ISO 178 MPa 135　65　
Charpy notched impact strength ISO 179/1eA kJ/m2 3.5　5　
Charpy unnotched impact strength ISO 179/1eU kJ/m2 20　NB
Izod notched impact strength ISO 180/1A kJ/m2 2.5　5　
Flamability 　 　 　 　
Flammability UL 94 (Thickness 1,6 mm) ISO 1210/UL 94 　 HB -
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　-
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 95　-
Coef. of Linear thermal expansion normal or perpendicular ( 23°C to 85°C) ISO 11359 E-5 / °C 6　-
Electrical 　 　 　 　
Dissipation factor IEC60250 　 0.02　0.11　
Volume resistivity IEC60093 Ohm.cm 50E13 10E13
Surface resistivity IEC60093 Ohm 50E13 50E10
Dielectric strength IEC60243 kV/mm 30　26　
Comparative tracking index sol. A IEC60112 Volt 600　500