PA66 49美国首诺Vydyne®冲击改性通用级尼龙66塑料（18024445500）

Physical Dry Conditioned Unit Test Method
Density 1.11　-- g/cm³ ISO 1183
Molding Shrinkage 　 　 　 ISO 294-4
Across Flow : 2.00 mm 1.6　-- % 　
Flow : 2.00 mm 1.8　-- % 　
Water Absorption (23°C, 24 hr) 1.3　-- % ISO 62
Water Absorption (Equilibrium, 50% RH) 2.3　-- % ISO 62
Mechanical Dry Conditioned Unit Test Method
Tensile Modulus 3040　2130　MPa ISO 527-2
Tensile Stress (Yield) 70.0　50.0　MPa ISO 527-2
Tensile Stress (Break) 46.0　42.0　MPa ISO 527-2
Tensile Strain (Break) 17　40　% ISO 527-2
Flexural Modulus 2600　890　MPa ISO 178
Flexural Stress 81.0　27.0　MPa ISO 178
Charpy Notched Impact Strength 　 　 　 ISO 179
-40°C 8.0　6.0　kJ/m² 　
-30°C 11　10　kJ/m² 　
23°C 13　43　kJ/m² 　
Charpy Unnotched Impact Strength 　 　 　 ISO 179
-30°C No Break No Break　 　
23°C No Break No Break　 　
Notched Izod Impact Strength 　 　 　 ISO 180
-40°C 8.0　10　kJ/m² 　
-30°C 9.0　15　kJ/m² 　
23°C 10　37　kJ/m² 　
Thermal Dry Conditioned Unit Test Method
Heat Deflection Temperature 　 　 　 ISO 75-2/B
0.45 MPa, Unannealed 202　-- °C 　
Heat Deflection Temperature 　 　 　 ISO 75-2/A
1.8 MPa, Unannealed 69.0　-- °C 　
Melting Temperature 260　-- °C ISO 11357-3
CLTE - Flow (23 to 55°C, 2.00 mm) 　 -- cm/cm/°C ISO 11359-2
CLTE - Transverse (23 to 55°C, 2.00 mm) 　 -- cm/cm/°C ISO 11359-2
RTI Elec 　 　 　 UL 746
0.750 mm 125　-- °C 　
1.50 mm 125　-- °C 　
3.00 mm 125　-- °C 　
RTI Imp 　 　 　 UL 746
0.750 mm 75.0　-- °C 　
1.50 mm 75.0　-- °C 　
3.00 mm 75.0　-- °C 　
RTI Str 　 　 　 UL 746
0.750 mm 85.0　-- °C 　
1.50 mm 85.0　-- °C 　
3.00 mm 85.0　-- °C 　
Volume Resistivity (0.750 mm) 　 -- ohm·cm IEC 60093
Dielectric Strength (1.00 mm) 23　-- kV/mm ASTM D149
Arc Resistance (3.00 mm) PLC 5 --　 ASTM D495
Comparative Tracking Index (3.00 mm) 600　-- V IEC 60112
High Amp Arc Ignition (HAI) 　 　 　 UL 746
0.750 mm PLC 0 --　 　
1.50 mm PLC 0 --　 　
3.00 mm PLC 0 --　 　
High Voltage Arc Tracking Rate (HVTR) PLC 1 --　 UL 746
Hot-wire Ignition (HWI) 　 　 　 UL 746
0.750 mm PLC 4 --　 　
1.50 mm PLC 4 --　 　
3.00 mm PLC 3 --　 　
Flammability Dry Conditioned Unit Test Method
Flame Rating 　 　 　 UL 94
0.750 mm HB --　 　
1.50 mm HB --　 　
3.00 mm HB --　 　
Glow Wire Flammability Index 　 　 　 IEC 60695-2-12
0.750 mm 700　-- °C 　
1.50 mm 750　-- °C 　
3.00 mm 700　-- °C 　
Glow Wire Ignition Temperature 　 　 　 IEC 60695-2-13
0.750 mm 725　-- °C 　
1.50 mm 775　-- °C 　
3.00 mm 725　-- °C 　
Injection 　 Dry Unit 　 　
Drying Temperature 　 80.0 °C　 　
Drying Time 　 4.0 hr　 　
Suggested Max Regrind 　 25 %　 　
Rear Temperature 　 280 to 310 °C　 　
Middle Temperature 　 280 to 310 °C　 　
Front Temperature 　 280 to 310 °C　 　
Nozzle Temperature 　 280 to 310 °C　 　
Processing (Melt) Temp 　 285 to 305 °C　 　
Mold Temperature 　 65.0 to 95.0 °C