PA6 BKV 130 CS DUS008 000000德国朗盛Durethan 30%玻纤增强耐冲击尼龙6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, improved impact strength



ISO Shortname: ISO 1874-PA 6-HI, GR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.25　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.75　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9200　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 145　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.5　
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75　
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 55　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10　
Izod impact strength 23 °C kJ/m² ISO 180-1U 65　
Izod impact strength -30 °C kJ/m² ISO 180-1U 60　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 12　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　
Flexural modulus 2 mm/min MPa ISO 178-A 8500　
Flexural strength 2 mm/min MPa ISO 178-A 245　
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.3