PA6 BKV 40 H2.0 901510德国朗盛Durethan 40%玻纤增强尼龙6塑料（18024445500）

PA 6, 40 % glass fibers, injection molding, heat-aging stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6, GHR, 14-120, GF40

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.16　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.85　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.03　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.07　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11900 7800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 195 130
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 85 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 70
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 20
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 18 24
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 13 11
Flexural modulus 2 mm/min MPa ISO 178-A 11200 7300
Flexural strength 2 mm/min MPa ISO 178-A 310 200
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 5.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 305 170