PA6 BKV 60 XF 900116德国朗盛Durethan 60%玻纤增强热老化稳定尼龙6塑料（18024445500）

PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized



ISO Shortname: ISO1874-PA 6, GHR, 10-220, GF60

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.25　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.52　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 20200 13000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 215 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.3 2.8
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 88　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15　
Izod impact strength 23 °C kJ/m² ISO 180-1U 80 75
Izod impact strength -30 °C kJ/m² ISO 180-1U 80　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15　
Flexural modulus 2 mm/min MPa ISO 178-A 18500 14000
Flexural strength 2 mm/min MPa ISO 178-A 350 230
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.6 2.8
C Puncture maximum force 23 °C N ISO 6603-2 1100　
C Puncture maximum force -30 °C N ISO 6603-2 950　
C Puncture energy 23 °C J ISO 6603-2 4.2　
C Puncture energy -30 °C J ISO 6603-2 3.4　

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 221　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 208　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 217　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.11　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.85　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1693　
Bulk density　kg/m³ ISO 60 760　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.20　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.