PA6 BKV 15 G H2.0 900051德国朗盛Durethan 15%玻纤增强耐候热老化稳定尼龙6塑料（18024445500）

PA 6-Copolymer, 15 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, weather stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6/66, GHR, 14-060, GF15

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.34　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.67　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.1　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.21　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6300 4000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 120 70
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 11
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 40 40
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 35 35
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA < 10 < 10
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 25 35
Izod impact strength -30 °C kJ/m² ISO 180-1U 20 25
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 5700 3500
Flexural strength 2 mm/min MPa ISO 178-A 185 125
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 7.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　100
C Puncture maximum force 23 °C N ISO 6603-2 560　
C Puncture maximum force -30 °C N ISO 6603-2 505　
C Puncture energy 23 °C J ISO 6603-2 2.0　
C Puncture energy -30 °C J ISO 6603-2 1.5　
Ball indentation hardness　N/mm² ISO 2039-1 190 95

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 218　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 180　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 210　
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 55　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 200　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.3　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8　
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB　
Burning behavior UL 94 3.2 mm Class UL 94 HB　
C Oxygen index Method A % ISO 4589-2 23　
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650　
Burning behavior US-FMVSS302　 ISO 3795 passed　
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 200　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.1 10
C Relative permittivity 1 MHz - IEC 60250 3.7 4.3
C Dissipation factor 100 Hz 10-4 IEC 60250 80 2200
C Dissipation factor 1 MHz 10-4 IEC 60250 180 700
C Volume resistivity　Ohm·m IEC 60093 1E11 1E09
C Surface resistivity　Ohm IEC 60093 1E15 1E13
C Electric strength 1 mm kV/mm IEC 60243-1 30 30
C Comparative tracking index CTI Solution A V IEC 60112 375　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 7.8　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.6　
C Density　kg/m³ ISO 1183 1240　
Bulk density　kg/m³ ISO 60 700　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 260-290　
Mold temperature　°C - 80-100　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.