PA6 ECO BKV 20 FN20 000000µÂ¹úÀÊÊ¢Durethan 20%²£Á§ÎÞ±×èȼÄáÁú6ËÜÁÏ£¨18024445500£©

PA 6, 20 % glass, injection molding, halogen free flame retardant, contains at least 15 % pre-consumer-recyclate



ISO Shortname: ISO 1874-PA 6, GFHR, 12-050, G20; ISO 1043-PA G FR (30)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 ¡ãC / MT 80 ¡ãC; 600 bar % ISO 294-4 0.8¡¡
C Molding shrinkage, transverse 60x60x2; 260 ¡ãC / MT 80 ¡ãC; 600 bar % ISO 294-4 0.8¡¡
Post- shrinkage, parallel 60x60x2; 120 ¡ãC; 4 h % ISO 294-4 0.2¡¡
Post- shrinkage, transverse 60x60x2; 120 ¡ãC; 4 h % ISO 294-4 0.2¡¡

Mechanical properties (23 ¡ãC/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5400 2300
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 76 40
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 27
C Charpy impact strength 23 ¡ãC kJ/m² ISO 179-1eU 35 75
C Charpy notched impact strength 23 ¡ãC kJ/m² ISO 179-1eA <10 <10
C Charpy notched impact strength -30 ¡ãC kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 ¡ãC kJ/m² ISO 180-1U 30 65
Izod notched impact strength 23 ¡ãC kJ/m² ISO 180-1A <10 <10
Izod notched impact strength -30 ¡ãC kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 5300 2300
Flexural strength 2 mm/min MPa ISO 178-A 140 62
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.8 7.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 135 50