PA6 BM 240 H2.0 901510德国朗盛Durethan 40%矿物热老化稳定低翘曲尼龙6塑料（18024445500）

PA 6, 40 % mineral, injection molding, heat-aging stabilized, low tendency to warp, isotopic properties

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6, GHR, 14-060, MD40

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.25　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.22　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.17　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6000 2200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 85 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 7.0 40
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 120 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 90 90
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA < 10 12
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 100 N
Izod impact strength -30 °C kJ/m² ISO 180-1U 75 85
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 5500 2100
Flexural strength 2 mm/min MPa ISO 178-A 150 60