PA6 C 30H1 V30 NATURAL/F法国罗地亚TECHNYL阻燃30%玻纤增强尼龙6塑料（18024445500）

Properties Standards Unit Values 　
　 　 　 d.a.m*. Cond.**
Physical 　 　 　 　
Water absorption (24 h at 23°C) ISO 62 % 0.95　-
Density ISO 1183-A g/cm3 1.62　-
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 0.60　-
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 0.80　-
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 　 0.75　-
Mechanical 　 　 　 　
Tensile modulus ISO 527 type 1 A MPa 11400　8050　
Elongation at break ISO 527 type 1 A % 1.80　6　
Tensile strength at break ISO 527 type 1 A MPa 114　85　
Charpy notched impact strength ISO 179/1eA kJ/m2 9　13　
Charpy unnotched impact strength ISO 179/1eU kJ/m2 37　40　
Flamability 　 　 　 　
Flammability UL 94 (Thickness 0,8 mm) ISO 1210/UL 94 　 V0 -
Flammability UL 94 (Thickness 1,6 mm) ISO 1210/UL 94 　 V0 -
Flammability UL 94 (Thickness 3,2 mm) ISO 1210/UL 94 　 V0 -
Glow wire flammability index (thickness = 0,8) IEC60695-2-12 °C 960　-
Glow wire flammability index (thickness = 1,6) IEC60695-2-12 °C 960　-
Glow wire ignition temperature (thickness = 0,8) IEC60695-2-13 °C 825　-
Glow wire ignition temperature (thickness = 1,6) IEC60695-2-13 °C 850　-
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 222　-
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 197　-
Electrical 　 　 　 　
Dissipation factor IEC60250 　 0.01　0.06　
Dielectric strength IEC60243 kV/mm 41　38　
Comparative tracking index sol. A IEC60112 Volt 450　-