PA6 C 216 V30 NATURAL法国罗地亚TECHNYL注塑级30%玻纤增强尼龙6塑料（18024445500）

　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 1,05 　
Density ISO 1183/A g/cm3 1,36 　
Molding shrinkage Parallel ISO 294-4 % 0,65 　
Molding shrinkage normal or perpendicular ISO 294-4 % 0,35 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 9600　6200　
Tensile strength at break ISO 527 Type 1A MPa 190　110　
Elongation at break ISO 527 Type 1A % 3,80 4,50
Flexural modulus ISO 178 MPa 8400　4900　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 15　31,5
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 100　108　
Izod notched impact strength (23 °C) ASTM D256 J/m 120　　
　 ISO 180/1A kJ/m2 14　24　
Flammability 　 　 　 　
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 　 HB 　
Flammability (Thickness: 3,2 mm) ISO 1210 / UL94 　 HB 　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 650　　
Limit Oxygen Index ISO 4589 　 23　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 222　　
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 210　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 205　　
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 3,2