PA66 103FHS BKB009美国杜邦Zytel®热稳定内部润滑聚酰胺66尼龙塑料（18024445500）

Zytel® 103FHS BKB009 is a heat stabilised, internally lubricated polyamide 66 resin for injection moulding. It was developed for fast
cycles and high productivity.
General information Value Unit Test Standard
Resin Identification PA66 - -
Part Marking Code >PA66< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage, parallel 1.3 / * % ISO 294-4, 2577
Moulding shrinkage, normal 1.3 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 3100 / - MPa ISO 527-1/-2
Yield stress 85 / - MPa ISO 527-1/-2
Yield strain 4.3 / - % ISO 527-1/-2
Nominal strain at break 15 / - % ISO 527-1/-2
Flexural Modulus 2800 / - MPa ISO 178
Charpy impact strength, 23°C 250 / - kJ/m² ISO 179/1eU
Charpy notched impact strength, 23°C 5 / - kJ/m² ISO 179/1eA
Izod notched impact strength 　 　 ISO 180/1A
23°C 5/- kJ/m² 　
-40°C 5/- kJ/m² 　
Izod impact strength, 23°C 200/- kJ/m² ISO 180/1U
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Temp. of deflection under load 　 　 ISO 75-1/-2
1.8 MPa 70 / * °C 　
0.45 MPa 195 / * °C 　
RTI, electrical 　 　 UL 746B
0.75 mm 140 / * °C 　
1.5mm 140 / * °C 　
RTI, impact 　 　 UL 746B
0.75 mm 95 °C 　
1.5mm 110 / * °C 　
RTI, strength 　 　 UL 746B
0.75 mm 115 °C 　
1.5mm 125 / * °C 　
Flammability dry / cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. V-2 / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h V-2 / * class IEC 60695-11-10
Thickness tested 0.71 / * mm IEC 60695-11-10
Glow Wire Flammability Index 　 　 IEC 60695-2-1/2
0.75mm 850 / - °C 　
1.5mm 960 / - °C 　
3mm 960 / - °C 　
Glow Wire Ignition Temperature 　 　 IEC 60695-2-1/3
0.75mm 725/- °C 　
1.5mm 725/- °C 　
3mm 725/- °C 　
Other properties dry/cond Unit Test Standard
Density 1140/- kg/m³ ISO 1183