PA66 RZL16沙伯基础创新耐磨聚酰胺66尼龙树脂（18024445500）

Also known as:LNP™LUBRICOMP™Compound RFL-4016 M

Product reorder name:RZL16

　

LNP™ LUBRICOMP™ RZL16 is a compound based on Nylon 66 resin containing 30% Milled Glass, 5% PTFE. Added feature of this grade is: Wear Resistant.

　






Property
　


TYPICAL PROPERTIES (1)

MECHANICAL
Value
Unit
Standard
　

Tensile Stress, yld, Type I, 5 mm/min
640
kgf/cm²
ASTM D 638
　

Tensile Stress, brk, Type I, 5 mm/min
630
kgf/cm²
ASTM D 638
　

Tensile Strain, yld, Type I, 5 mm/min
2.4
%
ASTM D 638
　

Tensile Strain, brk, Type I, 5 mm/min
3.2
%
ASTM D 638
　

Tensile Modulus, 5 mm/min
55200
kgf/cm²
ASTM D 638
　

Flexural Stress, brk, 1.3 mm/min, 50 mm span
1040
kgf/cm²
ASTM D 790
　

Flexural Modulus, 1.3 mm/min, 50 mm span
44900
kgf/cm²
ASTM D 790
　

Tensile Stress, yield, 5 mm/min
64
MPa
ISO 527
　

Tensile Stress, break, 5 mm/min
63
MPa
ISO 527
　

Tensile Strain, yield, 5 mm/min
2
%
ISO 527
　

Tensile Strain, break, 5 mm/min
3
%
ISO 527
　

Tensile Modulus, 1 mm/min
5380
MPa
ISO 527
　

Flexural Stress
90
MPa
ISO 178
　

Flexural Modulus, 2 mm/min
4500
MPa
ISO 178
　

IMPACT
Value
Unit
Standard
　

Izod Impact, unnotched, 23°C
19
cm-kgf/cm
ASTM D 4812
　

Izod Impact, notched, 23°C
3
cm-kgf/cm
ASTM D 256
　

Multiaxial Impact
14
cm-kgf
ISO 6603
　

Instrumented Impact Total Energy, 23°C
55
cm-kgf
ASTM D 3763
　

Izod Impact, unnotched 80*10*4 +23°C
19
kJ/m²
ISO 180/1U
　

Izod Impact, notched 80*10*4 +23°C
3
kJ/m²
ISO 180/1A
　

THERMAL
Value
Unit
Standard
　

HDT, 0.45 MPa, 3.2 mm, unannealed
248
°C
ASTM D 648
　

HDT, 1.82 MPa, 3.2mm, unannealed
215
°C
ASTM D 648
　

CTE, -30°C to 30°C, flow
5.5E-05
1/°C
ASTM D 696
　

CTE, -30°C to 30°C, xflow
6.2E-05
1/°C
ASTM D 696
　

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
239
°C
ISO 75/Bf
　

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
108
°C
ISO 75/Af
　

PHYSICAL
Value
Unit
Standard
　

Specific Gravity
1.4
-
ASTM D 792
　

Density
1.39
g/cm³
ASTM D 792
　

Moisture Absorption, 50% RH, 24 hrs
0.69
%
ASTM D 570
　

Mold Shrinkage, flow, 24 hrs (5)
1.8
%
ASTM D 955
　

Mold Shrinkage, xflow, 24 hrs (5)
1.4
%
ASTM D 955
　

Wear Factor Washer
44
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
　

Wear Factor Ring
3
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
　

Dynamic COF
0.49
-
ASTM D 3702 Modified
　

Static COF
0.53
-
ASTM D 3702 Modified
　

Moisture Absorption (23°C / 50% RH)
0.96
%
ISO 62
　


Source GMD, last updated:2015/01/06


Processing


Parameter

Injection Molding
Value
Unit

Drying Temperature
80
°C

Drying Time
4
hrs

Maximum Moisture Content
0.15 - 0.25
%

Melt Temperature
280 - 305
°C

Front - Zone 3 Temperature
295 - 305
°C

Middle - Zone 2 Temperature
280 - 295
°C

Rear - Zone 1 Temperature
265 - 275
°C

Mold Temperature
95 - 110
°C

Back Pressure
0.2 - 0.3
MPa

Screw Speed
30 - 60
rpm


Source GMD, last updated:2015/01/06


　
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.


供应的沙伯基础PA66塑料如下：
LNP™ LUBRICOMP Compound
　

Grades
Description

RA004
Internally Lubricated Nylon 66 compound containing Aramid.


RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.


RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.


RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.


RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.


RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.


RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:

RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.


RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.


RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.

RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.

RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.

RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.

RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,

RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.

RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.

RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.

RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).

RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).

RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.

RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.

RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).