PA66 AC 30 DUS027 000000德国朗盛Durethan耐热耐老化耐冲击尼龙66塑料（18024445500）

PA 66, non-reinforced, injection molding, heat-aging stabilized, improved impact strength



ISO Shortname: ISO 1874-PA 66-HI, GHR, 14-030

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.3　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.8　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3000 1100
C Yield stress 50 mm/min MPa ISO 527-1,-2 70 40
C Yield strain 50 mm/min % ISO 527-1,-2 5.8 25
C Nominal strain at break 50 mm/min % ISO 527-1,-2 18 75
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10 25
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m² ISO 180-1U N N
Izod impact strength -30 °C kJ/m² ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 25
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　
Flexural modulus 2 mm/min MPa ISO 178-A 2600 1000
Flexural strength 2 mm/min MPa ISO 178-A 100 40
Flexural strain at flexural strength 2 mm/min % ISO 178-A 6.6 8.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 80 30

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 261　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 66　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 192　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.1　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1110　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 270-290　
admissible residence time at Tmax　min - <=10　
Mold temperature　°C - 80-90　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.