PA66 AKV 15 FN 00 000000德国朗盛Durethan 12%玻纤无卤阻燃尼龙66塑料（18024445500）

PA 66, 12 % glass fibers, injection molding, halogen free flame retardant



ISO Shortname: ISO 1874-PA 66, GFHR, 14-060, GF12 ISO 1043:PA GF FR (30+40)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 270 °C; 2.16 kg cm³/(10 min) ISO 1133-1 25　
C Molding shrinkage, parallel 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 0.6　
C Molding shrinkage, transverse 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 1.0　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6500 3600
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 90 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.3 5.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 40 45
Izod impact strength 23 °C kJ/m² ISO 180-1U 35 40
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6400 3300
Flexural strength 2 mm/min MPa ISO 178-A 150 90
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.3 5.5

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 262　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 205　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 245　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 225　
Burning behavior UL 94 0.4 mm Class UL 94 V-0