PA66 AKV 30 000000德国朗盛Durethan 30%玻纤尼龙66塑料（18024445500）

PA 66, 30 % glass fibers, injection molding

ISO/ ASTM

ISO Shortname: ISO 1874-PA 66, GR, 14-110, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.35　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 1.46　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.05　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10600 7000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 185 125
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 70
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 15
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 8400 5900
Flexural strength 2 mm/min MPa ISO 178-A 290 200
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　165
Ball indentation hardness　N/mm² ISO 2039-1 230 130