PA66 AKV 50 H2.0 901510德国朗盛Durethan 50%玻纤热老化稳定注塑尼龙66塑料（18024445500）
PA 66, 50 % glass fibers, injection molding, heat-aging stabilized
ISO Shortname: ISO 1874-PA 66, GHR, 14-160, GF50
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.23
Molding shrinkage, transverse 150x105x3; 300 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.9
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.02
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.04
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16000 10200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 230 155
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.6 4.3
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 100 100
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 23
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 12 15
Izod impact strength 23 °C kJ/m² ISO 180-1U 85 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 85 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 12 12
Flexural modulus 2 mm/min MPa ISO 178-A 14000 10000
Flexural strength 2 mm/min MPa ISO 178-A 360 240
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 4.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 216
C Puncture maximum force 23 °C N ISO 6603-2 1162 1200
C Puncture maximum force -30 °C N ISO 6603-2 1050
C Puncture energy 23 °C J ISO 6603-2 3.6 5.0
C Puncture energy -30 °C J ISO 6603-2 2.8
Ball indentation hardness N/mm² ISO 2039-1 246 140 |