PA66 DP 2802/30 000000德国朗盛Durethan 30%玻纤无卤阻燃注塑尼龙66塑料（18024445500）

PA 66, 30 % glass fibers, injection molding, halogen free flame retardant



ISO Shortname: ISO 1874-PA 66, GF, 14-060, GF30; ISO 1043-PA GF FR (30)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 270 °C; 2.16 kg cm³/(10 min) ISO 1133-1 17　
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 6000 3900
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 85 56
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.5 13.2
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 35 60
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m² ISO 180-1U 30 50
Izod notched impact strength 23 °C kJ/m² ISO 180-1A < 10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6700 3700
Flexural strength 2 mm/min MPa ISO 178-A 170 90
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.3 6.5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 165 80
Ball indentation hardness　N/mm² ISO 2039-1 200