PA66 DP AKV 30 FN00 000000德国朗盛Durethan 30%玻纤无卤阻燃注塑尼龙66塑料（18024445500）

PA 66, 30 % glass fibers, injection molding, halogen free flame retardant



ISO Shortname: ISO 1874-PA 66, GFHR, 14-100, GF30, ISO 1043-PA GF FR (30+40)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 0.2　
C Molding shrinkage, transverse 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 0.7　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10500 6500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 135 85
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.8 5.4
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 65　
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10　
Izod impact strength 23 °C kJ/m² ISO 180-1U 55 57
Izod impact strength -30 °C kJ/m² ISO 180-1U 50　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10　
Flexural modulus 2 mm/min MPa ISO 178-A 9300 5600
Flexural strength 2 mm/min MPa ISO 178-A 215 135
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.1 5.2
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　120