PA6 BC 700 HTS DUSXBL 900116德国朗盛Durethan耐热耐冲击吹塑尼龙6塑料(18024445500)
PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability
ISO Shortname: ISO 1874-PA 6/66-HI, BHS, 14-010
Property Test Condition Unit Standard guide value
d.a.m. cond.
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 980 210
C Yield stress 50 mm/min MPa ISO 527-1,-2 28
C Yield strain 50 mm/min % ISO 527-1,-2 6.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 105
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 75
Izod impact strength 23 °C kJ/m² ISO 180-1U N N
Izod impact strength -30 °C kJ/m² ISO 180-1U N
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 90
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 70
Flexural modulus 2 mm/min MPa ISO 178-A 980 230
Flexural strength 2 mm/min MPa ISO 178-A 35 12
Flexural strain at flexural strength 2 mm/min % ISO 178-A 6.1 9
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 30 7
C Puncture maximum force 23 °C N ISO 6603-2 3300
C Puncture maximum force -30 °C N ISO 6603-2 4100
C Puncture energy 23 °C J ISO 6603-2 50
C Puncture energy -30 °C J ISO 6603-2 50
Shore hardness D - DIN EN ISO 868 65 59 |