PA6 BKV 115 H3.0 DUS008 000000德国朗盛Durethan 15%玻纤增强尼龙6塑料（18024445500）

PA 6, 15% glass fibers, injection molding, improved impact strength, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6-HI, GHR, 14-060, GF15

Property Test Condition Unit Standard guide value
d.a.m. cond.

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5600 2800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 115 65
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4 12
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 65 80
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 50　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10　
Flexural modulus 2 mm/min MPa ISO 178-A 4900 2500
Flexural strength 2 mm/min MPa ISO 178-A 185 95
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 165 70

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 195　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1228