PA6 BKV 315 Z H2.0 901510德国朗盛Durethan 15%玻纤增强吹塑耐热老化尼龙6塑料（18024445500）
PA 6, 15 % glass fibers, blow molding, improved impact strength, heat-aging stabilized
ISO Shortname: ISO 1874-PA 6-HI, BHR, 14-050, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.9
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.6
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.2
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5300 2500
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 105 55
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 5.0 19
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 105
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 85 90
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 30
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10 10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 65 95
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 70 65
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A 15 30
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A 10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 4800 2300 |