PA66 RX01514沙伯基础创新内部润滑含专用填料尼龙66塑料（18024445500）

Also known as:LNP™LUBRICOMP™Compound PDX-R-01514

Product reorder name:RX01514

　

LNP LUBRICOMP RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.

　






Property
　


TYPICAL PROPERTIES (1)

MECHANICAL
Value
Unit
Standard
　

Tensile Stress, yield
860
kgf/cm²
ASTM D 638
　

Tensile Stress, break
730
kgf/cm²
ASTM D 638
　

Tensile Strain, yield
4.2
%
ASTM D 638
　

Tensile Strain, break
21.1
%
ASTM D 638
　

Tensile Modulus, 50 mm/min
35100
kgf/cm²
ASTM D 638
　

Flexural Modulus
28100
kgf/cm²
ASTM D 790
　

Tensile Stress, yield
80
MPa
ISO 527
　

Tensile Stress, break
78
MPa
ISO 527
　

Tensile Strain, yield
3.9
%
ISO 527
　

Tensile Strain, break
19.1
%
ISO 527
　

Tensile Modulus, 1 mm/min
3400
MPa
ISO 527
　

Flexural Stress
96
MPa
ISO 178
　

Flexural Modulus
2800
MPa
ISO 178
　

IMPACT
Value
Unit
Standard
　

Izod Impact, unnotched, 23°C
193
cm-kgf/cm
ASTM D 4812
　

Izod Impact, notched, 23°C
4
cm-kgf/cm
ASTM D 256
　

Instrumented Impact Energy @ peak, 23°C
296
cm-kgf
ASTM D 3763
　

Multiaxial Impact
489
cm-kgf
ISO 6603
　

Izod Impact, unnotched 80*10*4 +23°C
251
kJ/m²
ISO 180/1U
　

Izod Impact, notched 80*10*4 +23°C
4
kJ/m²
ISO 180/1A
　

THERMAL
Value
Unit
Standard
　

HDT, 0.45 MPa, 3.2 mm, unannealed
183
°C
ASTM D 648
　

HDT, 1.82 MPa, 3.2mm, unannealed
66
°C
ASTM D 648
　

CTE, -40°C to 40°C, flow
8.28E-05
1/°C
ASTM E 831
　

CTE, -40°C to 40°C, xflow
8.64E-05
1/°C
ASTM E 831
　

CTE, -40°C to 40°C, flow
8.3E-05
1/°C
ISO 11359-2
　

CTE, -40°C to 40°C, xflow
8.7E-05
1/°C
ISO 11359-2
　

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
156
°C
ISO 75/Bf
　

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
62
°C
ISO 75/Af
　

PHYSICAL
Value
Unit
Standard
　

Density
1.15
g/cm³
ASTM D 792
　

Moisture Absorption, 50% RH, 24 hrs
1.1
%
ASTM D 570
　

Mold Shrinkage, flow, 24 hrs (5)
1 - 1.2
%
ASTM D 955
　

Mold Shrinkage, xflow, 24 hrs (5)
1.2 - 1.4
%
ASTM D 955
　

Mold Shrinkage, flow, 24 hrs (5)
1.1
%
ISO 294
　

Mold Shrinkage, xflow, 24 hrs (5)
1.3
%
ISO 294
　

Wear Factor Washer
67
10^-10 in^5-min/ft-lb-hr
ASTM D 3702 Modified
　

Dynamic COF
0.81
-
ASTM D 3702 Modified
　

Static COF
0.62
-
ASTM D 3702 Modified
　

Density
1.14
g/cm³
ISO 1183
　


Source GMD, last updated:2008/09/24


Processing


Parameter

Injection Molding
Value
Unit

Drying Temperature
80
°C

Drying Time
4
hrs

Maximum Moisture Content
0.15 - 0.25
%

Melt Temperature
275 - 290
°C

Front - Zone 3 Temperature
295 - 305
°C

Middle - Zone 2 Temperature
280 - 295
°C

Rear - Zone 1 Temperature
265 - 275
°C

Mold Temperature
80 - 95
°C

Back Pressure
0.2 - 0.3
MPa

Screw Speed
30 - 60
rpm


Source GMD, last updated:2008/09/24


　
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.


供应的沙伯基础PA66塑料如下：
LNP™ LUBRICOMP Compound
　

Grades
Description

RA004
Internally Lubricated Nylon 66 compound containing Aramid.


RAL22
Internally Lubricated Nylon 66 compound containing Aramid, PTFE.


RAL22I
Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.


RAL22S
Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.


RAL23
Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.


RAL23S
Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.


RCL36S
Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:

RCP36
Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.


RFL16
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL26S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.


RFL33
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.

RFL34
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.

RFL36L
Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.

RFP36
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.

RFP36XXZ
PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,

RN001S
Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.

RP003
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.

RP004
Internally Lubricated Nylon 66 compound containing PTFE, Silicone.

RX01514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).

RX03643H
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).

RX05496
Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.

RX06480
Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.

RX85514
Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).